TEM investigation of self-organized PbSe quantum dots as a function of spacer layer thickness and growth temperature

Logo poskytovatele

Varování

Publikace nespadá pod Fakultu sportovních studií, ale pod Přírodovědeckou fakultu. Oficiální stránka publikace je na webu muni.cz.
Autoři

KANG H.H. SPRINGHOLZ G. HOLY V. BAUER G.

Rok publikování 2001
Druh Článek v odborném periodiku
Časopis / Zdroj Materials Science and Engineering
Fakulta / Pracoviště MU

Přírodovědecká fakulta

Citace
Obor Fyzika pevných látek a magnetismus
Klíčová slova ISLANDS; SUPERLATTICES; STRAIN; GAAS
Popis PbSe quantum dot/PbEuTe superlattices were grown on PbTe/BaF2(111) using molecular beam epitaxy. The spacer thickness was varied From 32.4 to 312 nm and the growth temperature was 335 or 380 degreesC. Three different dot stacking sequences form with either vertical, face-centered cubic like or disordered stacking sequence along the [111] growth direction. The different stacking sequence can be controlled by the thickness of the spacer layer and the growth temperature, The dots are fully strained and the shape of the dots is either triangular pyramids or dome like depending on the spacer layer thickness. An analysis of the lateral and vertical correlation of the dots as well as the size and shape of the buried dots with respect to spacer thickness and growth temperature is presented.