Preparation of Hard Yet Moderately Ductile Mo2BC Thin Films by Pulsed-DC Magnetron Sputtering

Varování

Publikace nespadá pod Fakultu sportovních studií, ale pod Přírodovědeckou fakultu. Oficiální stránka publikace je na webu muni.cz.

Autoři	DEBNÁROVÁ Stanislava SOUČEK Pavel VAŠINA Petr ZÁBRANSKÝ Lukáš BURŠÍKOVÁ Vilma
Rok publikování	2016
Druh	Konferenční abstrakty
Fakulta / Pracoviště MU	Přírodovědecká fakulta
Citace
Popis	A thin film deposited on the surface of a tool can substantially influence its durability and performance. The most frequently used coatings in industry are ceramic coatings with great hardness and stiffness. However, these coatings are quite brittle, which can cause the formation and spreading of cracks. To prevent the formation of cracks, the material of the film should exhibit ductile behaviour. The combination of high hardness and moderate ductility has been discovered in the nanolaminate Mo2BC. Mid frequency pulsed-DC magnetron sputtering was used to deposit thin Mo2BC films. This method was chosen, because it is relatively simple and therefore industry-friendly.
Související projekty:	CEPLANT - Regionální VaV centrum pro nízkonákladové plazmové a nanotechnologické povrchové úpravy Lokální mikrostrukturní změny vyvolané statickou a dynamickou indentací nanostrukturovaných a nanolaminovaných povlaků Rozvoj centra pro nízkonákladové plazmové a nanotechnologické povrchové úpravy