Influence of Bonded Air- Versus Tin-side on the Shear Strength of Glass-to-Glass Joints of Transparent Epoxy Adhesive at Elevated Temperatures

Logo poskytovatele

Varování

Publikace nespadá pod Fakultu sportovních studií, ale pod Přírodovědeckou fakultu. Oficiální stránka publikace je na webu muni.cz.
Autoři

BOUTAR Yasmina ELIÁŠOVÁ Martina TICHÁ Petra KELAR TUČEKOVÁ Zlata KELAR Jakub

Rok publikování 2024
Druh Článek ve sborníku
Konference Challenging Glass 9 : Conference on Architectural and Structural Applications of Glass
Fakulta / Pracoviště MU

Přírodovědecká fakulta

Citace
www https://proceedings.challengingglass.com/index.php/cgc/article/view/497
Doi http://dx.doi.org/10.47982/cgc.9.497
Klíčová slova Float glass; Low-iron glass; Transparent adhesive; Air-side; Tin-side; Wettability; Shear strength; Elevated temperature
Popis Given the need to create a sustainable future with limited resources and growing environmental concerns, high-strength adhesives offer an alternative and potentially more efficient load-bearing connection to conventional bolted connections in glass structures. However, there is a lack of knowledge on the elevated-temperature effects on the mechanical strength of these connections. Therefore, in this paper, an experimental program was conducted to evaluate and compare the performance of transparent bonded glass joints. A transparent epoxy adhesive Loctite EA 9455 and two glass types (float and low-iron glass) were chosen to conduct experiments. The differences in surface wettability, between air and tin-sides were examined for both glass types. Results showed that water contact angle measurements on float glass sides were 39.25 % and 3.98 % higher than measurements for low-iron glass on air- and tin-sides respectively. Furthermore, tensile and shear tests were performed on bulk-cured adhesive samples and bonded glass-to-glass block shear specimens respectively, at room temperature (RT), 40 °C, and 80 °C. The results showed that tensile and shear strengths decreased with increasing temperatures. Furthermore, the shear strength was influenced by the surface properties of the glass sides. Indeed, results on air-side likewise tin-side of low-iron glass demonstrated higher resistance for all tested temperatures in comparison with the float glass.