PREPARATION OF [001] ORIENTED TITANIUM THIN FILM FOR MEMS APPLICATIONS BY KAUFMAN ION-BEAM SOURCE

Varování

Publikace nespadá pod Fakultu sportovních studií, ale pod Přírodovědeckou fakultu. Oficiální stránka publikace je na webu muni.cz.
Autoři

GABLECH I. CAHA Ondřej SVATOŠ V. PRÁŠEK J. PEKÁREK J. NEUŽIL P. ŠIKOLA Tomáš

Rok publikování 2018
Druh Článek ve sborníku
Konference 9TH INTERNATIONAL CONFERENCE ON NANOMATERIALS - RESEARCH & APPLICATION (NANOCON 2017)
Fakulta / Pracoviště MU

Přírodovědecká fakulta

Citace
Klíčová slova Titanium thin film; [001] orientation; stress-free; thermal coefficient of resistivity; resistivity
Popis We propose the sputtering deposition providing titanium thin films with controlled properties such as preferential crystallography and residual stress using Kaufman ion-beam source. The titanium thin films with thickness of approximate to 80 nm were deposited on [001] Si wafer covered by SiO2 deposited by plasma-enhanced chemical vapor deposition. To achieve the required crystallography and stress properties, we investigated the different beam voltage of Kaufman ion-beam source and controlled the substrate temperature during deposition using a built-in heater. We used two X-ray diffraction methods to determine the planes parallel to the sample surface and residual stress. We also measured the current-voltage curves to determine the resistivity (rho) and the thermal coefficient of resistivity (alpha) of titanium thin films at different substrate temperatures using 4-probe measurement setup. We showed that it is possible to prepare stress-free titanium thin films with pure [001] orientation at the lowest beam voltage of 200 V and substrate temperature of approximate to 273 degrees C. The corresponding lattice parameters a(0) and c(0) were (2.954 +/- 0.003) angstrom and (4.695 +/- 0.001) angstrom, respectively. Electrical parameters of this sample as rho and alpha were (9.2 +/- 0.1).10(-7) Omega.m and (2.6 +/- 0.2).10(-3) K-1, respectively. We found out that these layers are well suitable for micro-electro-mechanical systems where the pure [001] orientation, no residual stress and low rho and high alpha are essential. We found that rho and a are dependent on each other. The rho value was approximate to 2x higher than the bulk material value, which is an excellent result for a thin film with the thickness of approximate to 80 nm.